EN 1.5682 Steel vs. CC332G Bronze
EN 1.5682 steel belongs to the iron alloys classification, while CC332G bronze belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.5682 steel and the bottom bar is CC332G bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 230 | |
| 130 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 21 | |
| 22 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 72 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 620 |
| Tensile Strength: Yield (Proof), MPa | 570 | |
| 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 220 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1060 |
| Melting Onset (Solidus), °C | 1410 | |
| 1010 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 440 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.7 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.8 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.5 | |
| 29 |
| Density, g/cm3 | 7.9 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.3 | |
| 3.4 |
| Embodied Energy, MJ/kg | 31 | |
| 55 |
| Embodied Water, L/kg | 63 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 870 | |
| 270 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 24 | |
| 20 |
| Strength to Weight: Axial, points | 27 | |
| 21 |
| Strength to Weight: Bending, points | 23 | |
| 19 |
| Thermal Shock Resistance, points | 23 | |
| 21 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 8.5 to 10.5 |
| Carbon (C), % | 0 to 0.13 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 80 to 86 |
| Iron (Fe), % | 88.7 to 91.1 | |
| 1.0 to 3.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.1 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0.3 to 0.8 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 to 0.1 | |
| 0 |
| Nickel (Ni), % | 8.5 to 9.5 | |
| 1.5 to 4.0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 0.2 |
| Sulfur (S), % | 0 to 0.0050 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.2 |
| Vanadium (V), % | 0 to 0.050 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |