EN 1.5682 Steel vs. C92600 Bronze
EN 1.5682 steel belongs to the iron alloys classification, while C92600 bronze belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.5682 steel and the bottom bar is C92600 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 230 | |
| 70 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 21 | |
| 30 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 72 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 300 |
| Tensile Strength: Yield (Proof), MPa | 570 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 170 |
| Melting Completion (Liquidus), °C | 1450 | |
| 980 |
| Melting Onset (Solidus), °C | 1410 | |
| 840 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 370 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.7 | |
| 9.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.8 | |
| 9.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.5 | |
| 34 |
| Density, g/cm3 | 7.9 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.3 | |
| 3.6 |
| Embodied Energy, MJ/kg | 31 | |
| 58 |
| Embodied Water, L/kg | 63 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 | |
| 74 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 870 | |
| 88 |
| Stiffness to Weight: Axial, points | 13 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 27 | |
| 9.6 |
| Strength to Weight: Bending, points | 23 | |
| 11 |
| Thermal Shock Resistance, points | 23 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.25 |
| Carbon (C), % | 0 to 0.13 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 86 to 88.5 |
| Iron (Fe), % | 88.7 to 91.1 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 0.8 to 1.5 |
| Manganese (Mn), % | 0.3 to 0.8 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.1 | |
| 0 |
| Nickel (Ni), % | 8.5 to 9.5 | |
| 0 to 0.7 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.0050 | |
| 0 to 0.050 |
| Tin (Sn), % | 0 | |
| 9.3 to 10.5 |
| Vanadium (V), % | 0 to 0.050 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 1.3 to 2.5 |
| Residuals, % | 0 | |
| 0 to 0.7 |