EN 1.6212 Steel vs. AWS ER90S-B3

Both EN 1.6212 steel and AWS ER90S-B3 are iron alloys. They have a very high 96% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.6212 steel and the bottom bar is AWS ER90S-B3.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 27
19
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 470
690
Tensile Strength: Yield (Proof), MPa 310
620

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 50
40
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
4.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.8
Embodied Energy, MJ/kg 20
24
Embodied Water, L/kg 48
60

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
130
Resilience: Unit (Modulus of Resilience), kJ/m3 260
1000
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
25
Strength to Weight: Bending, points 17
22
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 14
20

Alloy Composition

Aluminum (Al), % 0.020 to 0.050
0
Carbon (C), % 0 to 0.14
0.070 to 0.12
Chromium (Cr), % 0
2.3 to 2.7
Copper (Cu), % 0
0 to 0.35
Iron (Fe), % 96.9 to 99.13
93.5 to 95.9
Manganese (Mn), % 0.7 to 1.5
0.4 to 0.7
Molybdenum (Mo), % 0
0.9 to 1.2
Nickel (Ni), % 0.15 to 0.8
0 to 0.2
Niobium (Nb), % 0 to 0.050
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.5
0.4 to 0.7
Sulfur (S), % 0 to 0.010
0 to 0.025
Vanadium (V), % 0 to 0.050
0
Residuals, % 0
0 to 0.5