EN 1.6212 Steel vs. EN 1.4736 Stainless Steel

Both EN 1.6212 steel and EN 1.4736 stainless steel are iron alloys. They have 80% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.6212 steel and the bottom bar is EN 1.4736 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 27
28
Fatigue Strength, MPa 230
230
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 310
370
Tensile Strength: Ultimate (UTS), MPa 470
580
Tensile Strength: Yield (Proof), MPa 310
310

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
1000
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 50
21
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
9.0
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 1.5
2.4
Embodied Energy, MJ/kg 20
35
Embodied Water, L/kg 48
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
140
Resilience: Unit (Modulus of Resilience), kJ/m3 260
250
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
21
Strength to Weight: Bending, points 17
20
Thermal Diffusivity, mm2/s 14
5.6
Thermal Shock Resistance, points 14
21

Alloy Composition

Aluminum (Al), % 0.020 to 0.050
1.7 to 2.1
Carbon (C), % 0 to 0.14
0 to 0.040
Chromium (Cr), % 0
17 to 18
Iron (Fe), % 96.9 to 99.13
77 to 81.1
Manganese (Mn), % 0.7 to 1.5
0 to 1.0
Nickel (Ni), % 0.15 to 0.8
0
Niobium (Nb), % 0 to 0.050
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0
0.2 to 0.8
Vanadium (V), % 0 to 0.050
0