EN 1.6217 Steel vs. Grade 11 Titanium

EN 1.6217 steel belongs to the iron alloys classification, while grade 11 titanium belongs to the titanium alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.6217 steel and the bottom bar is grade 11 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
120
Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 24
29
Fatigue Strength, MPa 280
170
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 73
38
Shear Strength, MPa 350
200
Tensile Strength: Ultimate (UTS), MPa 550
310
Tensile Strength: Yield (Proof), MPa 390
230

Thermal Properties

Latent Heat of Fusion, J/g 250
420
Maximum Temperature: Mechanical, °C 400
320
Melting Completion (Liquidus), °C 1460
1660
Melting Onset (Solidus), °C 1420
1610
Specific Heat Capacity, J/kg-K 470
540
Thermal Conductivity, W/m-K 50
22
Thermal Expansion, µm/m-K 13
9.2

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
3.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
7.3

Otherwise Unclassified Properties

Density, g/cm3 7.8
4.5
Embodied Carbon, kg CO2/kg material 1.5
47
Embodied Energy, MJ/kg 21
800
Embodied Water, L/kg 49
470

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
81
Resilience: Unit (Modulus of Resilience), kJ/m3 410
240
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
35
Strength to Weight: Axial, points 19
19
Strength to Weight: Bending, points 19
22
Thermal Diffusivity, mm2/s 14
8.9
Thermal Shock Resistance, points 16
22

Alloy Composition

Aluminum (Al), % 0.020 to 0.050
0
Carbon (C), % 0 to 0.16
0 to 0.080
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 96.6 to 99
0 to 0.2
Manganese (Mn), % 0.85 to 1.7
0
Nickel (Ni), % 0.15 to 0.85
0
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0
0 to 0.18
Palladium (Pd), % 0
0.12 to 0.25
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0
98.8 to 99.88
Vanadium (V), % 0 to 0.050
0
Residuals, % 0
0 to 0.4