EN 1.6217 Steel vs. C95820 Bronze

EN 1.6217 steel belongs to the iron alloys classification, while C95820 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.6217 steel and the bottom bar is C95820 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 24
15
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
44
Tensile Strength: Ultimate (UTS), MPa 550
730
Tensile Strength: Yield (Proof), MPa 390
310

Thermal Properties

Latent Heat of Fusion, J/g 250
230
Maximum Temperature: Mechanical, °C 400
230
Melting Completion (Liquidus), °C 1460
1080
Melting Onset (Solidus), °C 1420
1020
Specific Heat Capacity, J/kg-K 470
440
Thermal Conductivity, W/m-K 50
38
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
29
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 1.5
3.5
Embodied Energy, MJ/kg 21
56
Embodied Water, L/kg 49
380

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
86
Resilience: Unit (Modulus of Resilience), kJ/m3 410
400
Stiffness to Weight: Axial, points 13
8.0
Stiffness to Weight: Bending, points 24
20
Strength to Weight: Axial, points 19
24
Strength to Weight: Bending, points 19
22
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 16
25

Alloy Composition

Aluminum (Al), % 0.020 to 0.050
9.0 to 10
Carbon (C), % 0 to 0.16
0
Copper (Cu), % 0
77.5 to 82.5
Iron (Fe), % 96.6 to 99
4.0 to 5.0
Lead (Pb), % 0
0 to 0.020
Manganese (Mn), % 0.85 to 1.7
0 to 1.5
Nickel (Ni), % 0.15 to 0.85
4.5 to 5.8
Niobium (Nb), % 0 to 0.050
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.5
0 to 0.1
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
0 to 0.020
Vanadium (V), % 0 to 0.050
0
Zinc (Zn), % 0
0 to 0.2
Residuals, % 0
0 to 0.8