EN 1.6220 Steel vs. N07041 Nickel

EN 1.6220 steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is EN 1.6220 steel and the bottom bar is N07041 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Elongation at Break, % 23 to 25
14
Fatigue Strength, MPa 240 to 250
540
Tensile Strength: Ultimate (UTS), MPa 550 to 580
1400
Tensile Strength: Yield (Proof), MPa 340
1050

Thermal Properties

Melting Onset (Solidus), °C 1420
1320
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 52
11
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.2

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 120
180
Resilience: Unit (Modulus of Resilience), kJ/m3 300 to 310
2510
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19 to 20
47
Strength to Weight: Bending, points 19 to 20
34
Thermal Diffusivity, mm2/s 14
3.0
Thermal Shock Resistance, points 16 to 17
38