EN 1.6228 Steel vs. EN 1.0471 Steel

Both EN 1.6228 steel and EN 1.0471 steel are iron alloys. They have a very high 98% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.6228 steel and the bottom bar is EN 1.0471 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 25
23
Fatigue Strength, MPa 280
270
Impact Strength: V-Notched Charpy, J 65
38
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 360
360
Tensile Strength: Ultimate (UTS), MPa 570
580
Tensile Strength: Yield (Proof), MPa 390
380

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
2.2
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.5
Embodied Energy, MJ/kg 21
20
Embodied Water, L/kg 50
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
120
Resilience: Unit (Modulus of Resilience), kJ/m3 400
390
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
20
Strength to Weight: Bending, points 19
20
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 17
18

Alloy Composition

Aluminum (Al), % 0
0 to 0.060
Carbon (C), % 0 to 0.18
0 to 0.22
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 96.2 to 97.9
97.4 to 98.8
Manganese (Mn), % 0.8 to 1.5
1.0 to 1.5
Nickel (Ni), % 1.3 to 1.7
0
Niobium (Nb), % 0
0.015 to 0.1
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.35
0.15 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.010
Vanadium (V), % 0 to 0.050
0