EN 1.6308 Steel vs. S30615 Stainless Steel
Both EN 1.6308 steel and S30615 stainless steel are iron alloys. They have 63% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.6308 steel and the bottom bar is S30615 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 | |
| 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 23 | |
| 39 |
| Fatigue Strength, MPa | 320 | |
| 270 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 75 |
| Shear Strength, MPa | 390 | |
| 470 |
| Tensile Strength: Ultimate (UTS), MPa | 610 | |
| 690 |
| Tensile Strength: Yield (Proof), MPa | 460 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 340 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 960 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1370 |
| Melting Onset (Solidus), °C | 1420 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 500 |
| Thermal Conductivity, W/m-K | 39 | |
| 14 |
| Thermal Expansion, µm/m-K | 13 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.8 | |
| 19 |
| Density, g/cm3 | 7.9 | |
| 7.6 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 3.7 |
| Embodied Energy, MJ/kg | 22 | |
| 53 |
| Embodied Water, L/kg | 50 | |
| 170 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 | |
| 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 550 | |
| 260 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 22 | |
| 25 |
| Strength to Weight: Bending, points | 20 | |
| 23 |
| Thermal Diffusivity, mm2/s | 10 | |
| 3.7 |
| Thermal Shock Resistance, points | 18 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.8 to 1.5 |
| Carbon (C), % | 0 to 0.2 | |
| 0.16 to 0.24 |
| Chromium (Cr), % | 0 | |
| 17 to 19.5 |
| Iron (Fe), % | 96.4 to 97.9 | |
| 56.7 to 65.3 |
| Manganese (Mn), % | 1.2 to 1.6 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0.45 to 0.55 | |
| 0 |
| Nickel (Ni), % | 0.5 to 0.8 | |
| 13.5 to 16 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.4 | |
| 3.2 to 4.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 to 0.030 | |
| 0 |