EN 1.6368 Steel vs. EN 1.7386 Steel
Both EN 1.6368 steel and EN 1.7386 steel are iron alloys. They have a moderately high 90% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is EN 1.6368 steel and the bottom bar is EN 1.7386 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 210 | |
| 170 to 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 18 | |
| 18 to 21 |
| Fatigue Strength, MPa | 310 to 330 | |
| 170 to 290 |
| Impact Strength: V-Notched Charpy, J | 43 to 46 | |
| 38 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 75 |
| Shear Strength, MPa | 410 to 430 | |
| 340 to 410 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 690 | |
| 550 to 670 |
| Tensile Strength: Yield (Proof), MPa | 460 to 490 | |
| 240 to 440 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 600 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1450 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 40 | |
| 26 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.5 | |
| 9.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.4 | |
| 6.5 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 2.0 |
| Embodied Energy, MJ/kg | 22 | |
| 28 |
| Embodied Water, L/kg | 53 | |
| 88 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 92 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 580 to 650 | |
| 150 to 490 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 23 to 24 | |
| 20 to 24 |
| Strength to Weight: Bending, points | 21 to 22 | |
| 19 to 22 |
| Thermal Diffusivity, mm2/s | 11 | |
| 6.9 |
| Thermal Shock Resistance, points | 20 | |
| 15 to 18 |
Alloy Composition
| Aluminum (Al), % | 0.015 to 0.040 | |
| 0 to 0.040 |
| Carbon (C), % | 0 to 0.17 | |
| 0.080 to 0.15 |
| Chromium (Cr), % | 0 to 0.3 | |
| 8.0 to 10 |
| Copper (Cu), % | 0.5 to 0.8 | |
| 0 to 0.3 |
| Iron (Fe), % | 95.1 to 97.2 | |
| 86.8 to 90.5 |
| Manganese (Mn), % | 0.8 to 1.2 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 0.25 to 0.5 | |
| 0.9 to 1.1 |
| Nickel (Ni), % | 1.0 to 1.3 | |
| 0 |
| Niobium (Nb), % | 0.015 to 0.045 | |
| 0 |
| Nitrogen (N), % | 0 to 0.020 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.25 to 0.5 | |
| 0.25 to 1.0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.010 |