EN 1.6368 Steel vs. Reactor Grade Zirconium
EN 1.6368 steel belongs to the iron alloys classification, while reactor grade zirconium belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is EN 1.6368 steel and the bottom bar is reactor grade zirconium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 98 |
| Elongation at Break, % | 18 | |
| 21 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 690 | |
| 330 |
| Tensile Strength: Yield (Proof), MPa | 460 to 490 | |
| 160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 270 |
| Thermal Conductivity, W/m-K | 40 | |
| 22 |
| Thermal Expansion, µm/m-K | 13 | |
| 5.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.9 | |
| 6.5 |
| Embodied Water, L/kg | 53 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 56 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 580 to 650 | |
| 130 |
| Stiffness to Weight: Axial, points | 13 | |
| 8.4 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 23 to 24 | |
| 14 |
| Strength to Weight: Bending, points | 21 to 22 | |
| 16 |
| Thermal Diffusivity, mm2/s | 11 | |
| 13 |
| Thermal Shock Resistance, points | 20 | |
| 41 |
Alloy Composition
| Aluminum (Al), % | 0.015 to 0.040 | |
| 0 |
| Carbon (C), % | 0 to 0.17 | |
| 0 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0 |
| Copper (Cu), % | 0.5 to 0.8 | |
| 0 |
| Iron (Fe), % | 95.1 to 97.2 | |
| 0 |
| Manganese (Mn), % | 0.8 to 1.2 | |
| 0 |
| Molybdenum (Mo), % | 0.25 to 0.5 | |
| 0 |
| Nickel (Ni), % | 1.0 to 1.3 | |
| 0 |
| Niobium (Nb), % | 0.015 to 0.045 | |
| 0 |
| Nitrogen (N), % | 0 to 0.020 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0.25 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 99.7 to 100 |
| Residuals, % | 0 | |
| 0 to 0.27 |