EN 1.6368 Steel vs. SAE-AISI A2 Steel
Both EN 1.6368 steel and SAE-AISI A2 steel are iron alloys. They have a moderately high 93% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is EN 1.6368 steel and the bottom bar is SAE-AISI A2 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 690 | |
| 710 to 2040 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1450 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 40 | |
| 38 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.5 | |
| 8.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
| 9.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.4 | |
| 5.5 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 22 | |
| 38 |
| Embodied Water, L/kg | 53 | |
| 73 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 23 to 24 | |
| 25 to 73 |
| Strength to Weight: Bending, points | 21 to 22 | |
| 23 to 46 |
| Thermal Diffusivity, mm2/s | 11 | |
| 10 |
| Thermal Shock Resistance, points | 20 | |
| 25 to 71 |
Alloy Composition
| Aluminum (Al), % | 0.015 to 0.040 | |
| 0 |
| Carbon (C), % | 0 to 0.17 | |
| 1.0 to 1.1 |
| Chromium (Cr), % | 0 to 0.3 | |
| 4.8 to 5.5 |
| Copper (Cu), % | 0.5 to 0.8 | |
| 0 to 0.25 |
| Iron (Fe), % | 95.1 to 97.2 | |
| 89.4 to 93.3 |
| Manganese (Mn), % | 0.8 to 1.2 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.25 to 0.5 | |
| 0.9 to 1.4 |
| Nickel (Ni), % | 1.0 to 1.3 | |
| 0 to 0.3 |
| Niobium (Nb), % | 0.015 to 0.045 | |
| 0 |
| Nitrogen (N), % | 0 to 0.020 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.25 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 0.15 to 0.5 |