EN 1.6523 Steel vs. ASTM A182 Grade F122

Both EN 1.6523 steel and ASTM A182 grade F122 are iron alloys. They have 86% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.6523 steel and the bottom bar is ASTM A182 grade F122.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 190
220
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 510 to 1460
710

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 410
600
Melting Completion (Liquidus), °C 1460
1490
Melting Onset (Solidus), °C 1420
1440
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
24
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
10
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
12

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
12
Density, g/cm3 7.9
8.0
Embodied Carbon, kg CO2/kg material 1.5
3.0
Embodied Energy, MJ/kg 20
44
Embodied Water, L/kg 50
100

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18 to 52
25
Strength to Weight: Bending, points 18 to 36
22
Thermal Diffusivity, mm2/s 10
6.4
Thermal Shock Resistance, points 15 to 43
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Boron (B), % 0
0 to 0.0050
Carbon (C), % 0.17 to 0.23
0.070 to 0.14
Chromium (Cr), % 0.35 to 0.7
10 to 11.5
Copper (Cu), % 0 to 0.25
0.3 to 1.7
Iron (Fe), % 96.6 to 98.3
81.3 to 87.7
Manganese (Mn), % 0.65 to 1.0
0 to 0.7
Molybdenum (Mo), % 0.15 to 0.25
0.25 to 0.6
Nickel (Ni), % 0.4 to 0.7
0 to 0.5
Niobium (Nb), % 0
0.040 to 0.1
Nitrogen (N), % 0
0.040 to 0.1
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.3
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
1.5 to 2.5
Vanadium (V), % 0
0.15 to 0.3
Zirconium (Zr), % 0
0 to 0.010