EN 1.6526 Steel vs. EN 1.7201 Steel
Both EN 1.6526 steel and EN 1.7201 steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is EN 1.6526 steel and the bottom bar is EN 1.7201 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 190 | |
| 130 to 160 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 1460 | |
| 430 to 1300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 420 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 39 | |
| 45 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.6 | |
| 2.5 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.5 |
| Embodied Energy, MJ/kg | 20 | |
| 20 |
| Embodied Water, L/kg | 50 | |
| 51 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 18 to 52 | |
| 15 to 46 |
| Strength to Weight: Bending, points | 18 to 36 | |
| 16 to 34 |
| Thermal Diffusivity, mm2/s | 10 | |
| 12 |
| Thermal Shock Resistance, points | 15 to 43 | |
| 13 to 38 |
Alloy Composition
| Carbon (C), % | 0.17 to 0.23 | |
| 0.1 to 0.15 |
| Chromium (Cr), % | 0.35 to 0.7 | |
| 0.9 to 1.2 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.25 |
| Iron (Fe), % | 96.6 to 98.3 | |
| 96.9 to 98.3 |
| Manganese (Mn), % | 0.65 to 1.0 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 0.15 to 0.25 | |
| 0.15 to 0.25 |
| Nickel (Ni), % | 0.4 to 0.7 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.3 |
| Sulfur (S), % | 0.020 to 0.040 | |
| 0 to 0.025 |