EN 1.6526 Steel vs. CC496K Bronze

EN 1.6526 steel belongs to the iron alloys classification, while CC496K bronze belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.6526 steel and the bottom bar is CC496K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 190
72
Elastic (Young's, Tensile) Modulus, GPa 190
97
Poisson's Ratio 0.29
0.35
Shear Modulus, GPa 73
36
Tensile Strength: Ultimate (UTS), MPa 520 to 1460
210

Thermal Properties

Latent Heat of Fusion, J/g 250
170
Maximum Temperature: Mechanical, °C 410
140
Melting Completion (Liquidus), °C 1460
900
Melting Onset (Solidus), °C 1420
820
Specific Heat Capacity, J/kg-K 470
340
Thermal Conductivity, W/m-K 39
52
Thermal Expansion, µm/m-K 13
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
11
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
11

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
31
Density, g/cm3 7.9
9.2
Embodied Carbon, kg CO2/kg material 1.5
3.3
Embodied Energy, MJ/kg 20
52
Embodied Water, L/kg 50
380

Common Calculations

Stiffness to Weight: Axial, points 13
5.9
Stiffness to Weight: Bending, points 24
17
Strength to Weight: Axial, points 18 to 52
6.5
Strength to Weight: Bending, points 18 to 36
8.6
Thermal Diffusivity, mm2/s 10
17
Thermal Shock Resistance, points 15 to 43
8.1

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Antimony (Sb), % 0
0 to 0.5
Carbon (C), % 0.17 to 0.23
0
Chromium (Cr), % 0.35 to 0.7
0
Copper (Cu), % 0 to 0.25
72 to 79.5
Iron (Fe), % 96.6 to 98.3
0 to 0.25
Lead (Pb), % 0
13 to 17
Manganese (Mn), % 0.65 to 1.0
0 to 0.2
Molybdenum (Mo), % 0.15 to 0.25
0
Nickel (Ni), % 0.4 to 0.7
0.5 to 2.0
Phosphorus (P), % 0 to 0.025
0 to 0.1
Silicon (Si), % 0 to 0.3
0 to 0.010
Sulfur (S), % 0.020 to 0.040
0 to 0.1
Tin (Sn), % 0
6.0 to 8.0
Zinc (Zn), % 0
0 to 2.0