EN 1.6553 Steel vs. Chromium 33
EN 1.6553 steel belongs to the iron alloys classification, while chromium 33 belongs to the otherwise unclassified metals. They have a modest 34% of their average alloy composition in common, which, by itself, doesn't mean much. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is EN 1.6553 steel and the bottom bar is chromium 33.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 19 to 21 | |
| 45 |
| Poisson's Ratio | 0.29 | |
| 0.27 |
| Shear Modulus, GPa | 73 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 710 to 800 | |
| 850 |
| Tensile Strength: Yield (Proof), MPa | 470 to 670 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 320 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.7 | |
| 36 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 6.0 |
| Embodied Energy, MJ/kg | 21 | |
| 84 |
| Embodied Water, L/kg | 51 | |
| 250 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 150 | |
| 320 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 600 to 1190 | |
| 450 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 25 to 28 | |
| 30 |
| Strength to Weight: Bending, points | 23 to 24 | |
| 25 |
| Thermal Shock Resistance, points | 21 to 23 | |
| 21 |
Alloy Composition
| Carbon (C), % | 0.23 to 0.28 | |
| 0 to 0.015 |
| Chromium (Cr), % | 0.4 to 0.8 | |
| 31 to 35 |
| Copper (Cu), % | 0 to 0.3 | |
| 0.3 to 1.2 |
| Iron (Fe), % | 95.6 to 98.2 | |
| 25.7 to 37.9 |
| Manganese (Mn), % | 0.6 to 1.0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0.15 to 0.3 | |
| 0.5 to 2.0 |
| Nickel (Ni), % | 0.4 to 0.8 | |
| 30 to 33 |
| Nitrogen (N), % | 0 | |
| 0.35 to 0.6 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.8 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.010 |
| Vanadium (V), % | 0 to 0.030 | |
| 0 |