EN 1.6553 Steel vs. EN 1.4874 Stainless Steel

Both EN 1.6553 steel and EN 1.4874 stainless steel are iron alloys. They have a modest 34% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.6553 steel and the bottom bar is EN 1.4874 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 240
140
Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 19 to 21
6.7
Fatigue Strength, MPa 330 to 460
180
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 710 to 800
480
Tensile Strength: Yield (Proof), MPa 470 to 670
360

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 420
1150
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 39
13
Thermal Expansion, µm/m-K 13
15

Otherwise Unclassified Properties

Base Metal Price, % relative 2.7
70
Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 1.6
7.6
Embodied Energy, MJ/kg 21
110
Embodied Water, L/kg 51
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130 to 150
29
Resilience: Unit (Modulus of Resilience), kJ/m3 600 to 1190
310
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 28
16
Strength to Weight: Bending, points 23 to 24
16
Thermal Diffusivity, mm2/s 10
3.3
Thermal Shock Resistance, points 21 to 23
11

Alloy Composition

Carbon (C), % 0.23 to 0.28
0.35 to 0.65
Chromium (Cr), % 0.4 to 0.8
19 to 22
Cobalt (Co), % 0
18.5 to 22
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 95.6 to 98.2
23 to 38.9
Manganese (Mn), % 0.6 to 1.0
0 to 2.0
Molybdenum (Mo), % 0.15 to 0.3
2.5 to 3.0
Nickel (Ni), % 0.4 to 0.8
18 to 22
Niobium (Nb), % 0
0.75 to 1.3
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.8
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030
Tungsten (W), % 0
2.0 to 3.0
Vanadium (V), % 0 to 0.030
0