EN 1.6553 Steel vs. EN 2.4663 Nickel
EN 1.6553 steel belongs to the iron alloys classification, while EN 2.4663 nickel belongs to the nickel alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.6553 steel and the bottom bar is EN 2.4663 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 19 to 21 | |
| 40 |
| Fatigue Strength, MPa | 330 to 460 | |
| 250 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 710 to 800 | |
| 780 |
| Tensile Strength: Yield (Proof), MPa | 470 to 670 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 1010 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1430 |
| Melting Onset (Solidus), °C | 1420 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Conductivity, W/m-K | 39 | |
| 13 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.5 | |
| 1.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
| 1.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.7 | |
| 75 |
| Density, g/cm3 | 7.8 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 11 |
| Embodied Energy, MJ/kg | 21 | |
| 140 |
| Embodied Water, L/kg | 51 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 150 | |
| 250 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 600 to 1190 | |
| 230 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 25 to 28 | |
| 25 |
| Strength to Weight: Bending, points | 23 to 24 | |
| 22 |
| Thermal Diffusivity, mm2/s | 10 | |
| 3.5 |
| Thermal Shock Resistance, points | 21 to 23 | |
| 22 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.7 to 1.4 |
| Boron (B), % | 0 | |
| 0 to 0.0060 |
| Carbon (C), % | 0.23 to 0.28 | |
| 0.050 to 0.1 |
| Chromium (Cr), % | 0.4 to 0.8 | |
| 20 to 23 |
| Cobalt (Co), % | 0 | |
| 11 to 14 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 to 0.5 |
| Iron (Fe), % | 95.6 to 98.2 | |
| 0 to 2.0 |
| Manganese (Mn), % | 0.6 to 1.0 | |
| 0 to 0.2 |
| Molybdenum (Mo), % | 0.15 to 0.3 | |
| 8.5 to 10 |
| Nickel (Ni), % | 0.4 to 0.8 | |
| 48 to 59.6 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 0.8 | |
| 0 to 0.2 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0.2 to 0.6 |
| Vanadium (V), % | 0 to 0.030 | |
| 0 |