EN 1.6554 Steel vs. R30816 Cobalt
EN 1.6554 steel belongs to the iron alloys classification, while R30816 cobalt belongs to the cobalt alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.6554 steel and the bottom bar is R30816 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 230 to 280 | |
| 280 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 17 to 21 | |
| 23 |
| Fatigue Strength, MPa | 380 to 520 | |
| 250 |
| Poisson's Ratio | 0.29 | |
| 0.3 |
| Shear Modulus, GPa | 73 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 780 to 930 | |
| 1020 |
| Tensile Strength: Yield (Proof), MPa | 550 to 790 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 300 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1540 |
| Melting Onset (Solidus), °C | 1420 | |
| 1460 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 420 |
| Thermal Conductivity, W/m-K | 40 | |
| 13 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.9 | |
| 9.1 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 20 |
| Embodied Energy, MJ/kg | 22 | |
| 320 |
| Embodied Water, L/kg | 53 | |
| 440 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 150 | |
| 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 810 to 1650 | |
| 510 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 22 |
| Strength to Weight: Axial, points | 27 to 33 | |
| 31 |
| Strength to Weight: Bending, points | 24 to 27 | |
| 25 |
| Thermal Diffusivity, mm2/s | 11 | |
| 3.3 |
| Thermal Shock Resistance, points | 23 to 27 | |
| 28 |
Alloy Composition
| Carbon (C), % | 0.23 to 0.28 | |
| 0.32 to 0.42 |
| Chromium (Cr), % | 0.7 to 0.9 | |
| 19 to 21 |
| Cobalt (Co), % | 0 | |
| 40 to 49.8 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 94.6 to 97.3 | |
| 0 to 5.0 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 1.0 to 2.0 |
| Molybdenum (Mo), % | 0.2 to 0.3 | |
| 3.5 to 4.5 |
| Nickel (Ni), % | 1.0 to 2.0 | |
| 19 to 21 |
| Niobium (Nb), % | 0 | |
| 3.5 to 4.5 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.030 |
| Tantalum (Ta), % | 0 | |
| 3.5 to 4.5 |
| Tungsten (W), % | 0 | |
| 3.5 to 4.5 |
| Vanadium (V), % | 0 to 0.030 | |
| 0 |