EN 1.6570 Steel vs. S15500 Stainless Steel
Both EN 1.6570 steel and S15500 stainless steel are iron alloys. They have 80% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.6570 steel and the bottom bar is S15500 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 270 to 340 | |
290 to 430 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 11 to 17 | |
6.8 to 16 |
Fatigue Strength, MPa | 500 to 660 | |
350 to 650 |
Impact Strength: V-Notched Charpy, J | 40 to 48 | |
7.8 to 53 |
Poisson's Ratio | 0.29 | |
0.28 |
Shear Modulus, GPa | 73 | |
75 |
Tensile Strength: Ultimate (UTS), MPa | 910 to 1130 | |
890 to 1490 |
Tensile Strength: Yield (Proof), MPa | 760 to 1060 | |
590 to 1310 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
280 |
Maximum Temperature: Mechanical, °C | 440 | |
820 |
Melting Completion (Liquidus), °C | 1460 | |
1430 |
Melting Onset (Solidus), °C | 1420 | |
1380 |
Specific Heat Capacity, J/kg-K | 470 | |
480 |
Thermal Conductivity, W/m-K | 40 | |
17 |
Thermal Expansion, µm/m-K | 13 | |
11 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.7 | |
2.2 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 | |
2.5 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 3.9 | |
13 |
Density, g/cm3 | 7.9 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 1.7 | |
2.7 |
Embodied Energy, MJ/kg | 23 | |
39 |
Embodied Water, L/kg | 56 | |
130 |
Common Calculations
PREN (Pitting Resistance) | 2.5 | |
15 |
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 to 140 | |
98 to 120 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 1520 to 3010 | |
890 to 4460 |
Stiffness to Weight: Axial, points | 13 | |
14 |
Stiffness to Weight: Bending, points | 24 | |
25 |
Strength to Weight: Axial, points | 32 to 40 | |
32 to 53 |
Strength to Weight: Bending, points | 27 to 31 | |
26 to 37 |
Thermal Diffusivity, mm2/s | 11 | |
4.6 |
Thermal Shock Resistance, points | 27 to 33 | |
30 to 50 |
Alloy Composition
Carbon (C), % | 0.28 to 0.35 | |
0 to 0.070 |
Chromium (Cr), % | 1.0 to 1.4 | |
14 to 15.5 |
Copper (Cu), % | 0 | |
2.5 to 4.5 |
Iron (Fe), % | 94 to 96.2 | |
71.9 to 79.9 |
Manganese (Mn), % | 0.6 to 1.0 | |
0 to 1.0 |
Molybdenum (Mo), % | 0.3 to 0.5 | |
0 |
Nickel (Ni), % | 1.6 to 2.1 | |
3.5 to 5.5 |
Niobium (Nb), % | 0 | |
0.15 to 0.45 |
Phosphorus (P), % | 0 to 0.020 | |
0 to 0.040 |
Silicon (Si), % | 0 to 0.6 | |
0 to 1.0 |
Sulfur (S), % | 0 to 0.015 | |
0 to 0.030 |