EN 1.6570 Steel vs. ZA-12
EN 1.6570 steel belongs to the iron alloys classification, while ZA-12 belongs to the zinc alloys. There are 30 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.6570 steel and the bottom bar is ZA-12.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 270 to 340 | |
| 89 to 100 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 83 |
| Elongation at Break, % | 11 to 17 | |
| 1.6 to 5.3 |
| Fatigue Strength, MPa | 500 to 660 | |
| 73 to 120 |
| Poisson's Ratio | 0.29 | |
| 0.26 |
| Shear Modulus, GPa | 73 | |
| 33 |
| Tensile Strength: Ultimate (UTS), MPa | 910 to 1130 | |
| 260 to 400 |
| Tensile Strength: Yield (Proof), MPa | 760 to 1060 | |
| 210 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 120 |
| Maximum Temperature: Mechanical, °C | 440 | |
| 100 |
| Melting Completion (Liquidus), °C | 1460 | |
| 430 |
| Melting Onset (Solidus), °C | 1420 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Conductivity, W/m-K | 40 | |
| 120 |
| Thermal Expansion, µm/m-K | 13 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.7 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 | |
| 42 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.9 | |
| 11 |
| Density, g/cm3 | 7.9 | |
| 6.0 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 3.4 |
| Embodied Energy, MJ/kg | 23 | |
| 64 |
| Embodied Water, L/kg | 56 | |
| 440 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 to 140 | |
| 4.0 to 20 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1520 to 3010 | |
| 260 to 620 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 32 to 40 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 27 to 31 | |
| 15 to 20 |
| Thermal Diffusivity, mm2/s | 11 | |
| 43 |
| Thermal Shock Resistance, points | 27 to 33 | |
| 9.4 to 14 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 10.5 to 11.5 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Carbon (C), % | 0.28 to 0.35 | |
| 0 |
| Chromium (Cr), % | 1.0 to 1.4 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0.5 to 1.2 |
| Iron (Fe), % | 94 to 96.2 | |
| 0 to 0.075 |
| Lead (Pb), % | 0 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0 | |
| 0.015 to 0.030 |
| Manganese (Mn), % | 0.6 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 0.3 to 0.5 | |
| 0 |
| Nickel (Ni), % | 1.6 to 2.1 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 to 0.060 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Zinc (Zn), % | 0 | |
| 87.1 to 89 |