EN 1.6579 Steel vs. EN 1.8865 Steel

Both EN 1.6579 steel and EN 1.8865 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.6579 steel and the bottom bar is EN 1.8865 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260 to 290
200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 14
19
Fatigue Strength, MPa 380 to 570
340
Impact Strength: V-Notched Charpy, J 35 to 41
110
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 850 to 980
660
Tensile Strength: Yield (Proof), MPa 600 to 910
500

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 440
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
39
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 3.7
3.2
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.7
1.8
Embodied Energy, MJ/kg 22
24
Embodied Water, L/kg 56
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100 to 120
120
Resilience: Unit (Modulus of Resilience), kJ/m3 950 to 2210
670
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 30 to 35
23
Strength to Weight: Bending, points 25 to 28
21
Thermal Diffusivity, mm2/s 11
10
Thermal Shock Resistance, points 25 to 29
19

Alloy Composition

Boron (B), % 0
0 to 0.0050
Carbon (C), % 0.32 to 0.38
0 to 0.18
Chromium (Cr), % 1.4 to 1.7
0 to 1.0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 94.2 to 96.1
93.6 to 100
Manganese (Mn), % 0.6 to 1.0
0 to 1.7
Molybdenum (Mo), % 0.15 to 0.35
0 to 0.7
Nickel (Ni), % 1.4 to 1.7
0 to 1.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.6
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.0050
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0 to 0.080
Zirconium (Zr), % 0
0 to 0.15