EN 1.6579 steel belongs to the iron alloys classification, while CC765S brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.6579 steel and the bottom bar is CC765S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260 to 290
130
Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 11 to 14
21
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 73
42
Tensile Strength: Ultimate (UTS), MPa 850 to 980
540
Tensile Strength: Yield (Proof), MPa 600 to 910
220

Thermal Properties

Latent Heat of Fusion, J/g 250
180
Maximum Temperature: Mechanical, °C 440
140
Melting Completion (Liquidus), °C 1460
860
Melting Onset (Solidus), °C 1410
820
Specific Heat Capacity, J/kg-K 470
400
Thermal Conductivity, W/m-K 39
91
Thermal Expansion, µm/m-K 13
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
30
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
34

Otherwise Unclassified Properties

Base Metal Price, % relative 3.7
24
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.7
3.0
Embodied Energy, MJ/kg 22
51
Embodied Water, L/kg 56
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100 to 120
90
Resilience: Unit (Modulus of Resilience), kJ/m3 950 to 2210
220
Stiffness to Weight: Axial, points 13
7.6
Stiffness to Weight: Bending, points 24
20
Strength to Weight: Axial, points 30 to 35
19
Strength to Weight: Bending, points 25 to 28
18
Thermal Diffusivity, mm2/s 11
28
Thermal Shock Resistance, points 25 to 29
17

Alloy Composition

Aluminum (Al), % 0
0.5 to 2.5
Antimony (Sb), % 0
0 to 0.080
Carbon (C), % 0.32 to 0.38
0
Chromium (Cr), % 1.4 to 1.7
0
Copper (Cu), % 0
51 to 65
Iron (Fe), % 94.2 to 96.1
0.5 to 2.0
Lead (Pb), % 0
0 to 0.5
Manganese (Mn), % 0.6 to 1.0
0.3 to 3.0
Molybdenum (Mo), % 0.15 to 0.35
0
Nickel (Ni), % 1.4 to 1.7
0 to 6.0
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.6
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 1.0
Zinc (Zn), % 0
19.8 to 47.7