EN 1.6579 Steel vs. SAE-AISI 1146 Steel
Both EN 1.6579 steel and SAE-AISI 1146 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.6579 steel and the bottom bar is SAE-AISI 1146 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 260 to 290 | |
| 190 to 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 11 to 14 | |
| 13 to 17 |
| Fatigue Strength, MPa | 380 to 570 | |
| 240 to 400 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 850 to 980 | |
| 670 to 730 |
| Tensile Strength: Yield (Proof), MPa | 600 to 910 | |
| 360 to 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 440 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 39 | |
| 51 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.7 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.7 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 1.4 |
| Embodied Energy, MJ/kg | 22 | |
| 18 |
| Embodied Water, L/kg | 56 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 to 120 | |
| 93 to 97 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 950 to 2210 | |
| 340 to 1050 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 30 to 35 | |
| 24 to 26 |
| Strength to Weight: Bending, points | 25 to 28 | |
| 22 to 23 |
| Thermal Diffusivity, mm2/s | 11 | |
| 14 |
| Thermal Shock Resistance, points | 25 to 29 | |
| 20 to 22 |
Alloy Composition
| Carbon (C), % | 0.32 to 0.38 | |
| 0.42 to 0.49 |
| Chromium (Cr), % | 1.4 to 1.7 | |
| 0 |
| Iron (Fe), % | 94.2 to 96.1 | |
| 98.3 to 98.8 |
| Manganese (Mn), % | 0.6 to 1.0 | |
| 0.7 to 1.0 |
| Molybdenum (Mo), % | 0.15 to 0.35 | |
| 0 |
| Nickel (Ni), % | 1.4 to 1.7 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0.080 to 0.13 |