EN 1.6579 Steel vs. SAE-AISI P20 Steel
Both EN 1.6579 steel and SAE-AISI P20 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.6579 steel and the bottom bar is SAE-AISI P20 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 850 to 980 | |
| 540 to 1050 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 39 | |
| 45 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.7 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.7 | |
| 2.8 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 1.6 |
| Embodied Energy, MJ/kg | 22 | |
| 21 |
| Embodied Water, L/kg | 56 | |
| 52 |
Common Calculations
| PREN (Pitting Resistance) | 2.4 | |
| 2.6 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 30 to 35 | |
| 19 to 37 |
| Strength to Weight: Bending, points | 25 to 28 | |
| 19 to 29 |
| Thermal Diffusivity, mm2/s | 11 | |
| 12 |
| Thermal Shock Resistance, points | 25 to 29 | |
| 18 to 35 |
Alloy Composition
| Carbon (C), % | 0.32 to 0.38 | |
| 0.28 to 0.4 |
| Chromium (Cr), % | 1.4 to 1.7 | |
| 0.4 to 2.0 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 94.2 to 96.1 | |
| 95.2 to 98.5 |
| Manganese (Mn), % | 0.6 to 1.0 | |
| 0.35 to 0.71 |
| Molybdenum (Mo), % | 0.15 to 0.35 | |
| 0.3 to 0.55 |
| Nickel (Ni), % | 1.4 to 1.7 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.6 | |
| 0.2 to 0.8 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |