EN 1.6579 Steel vs. C82800 Copper
EN 1.6579 steel belongs to the iron alloys classification, while C82800 copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.6579 steel and the bottom bar is C82800 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 11 to 14 | |
| 1.0 to 20 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 73 | |
| 46 |
| Tensile Strength: Ultimate (UTS), MPa | 850 to 980 | |
| 670 to 1140 |
| Tensile Strength: Yield (Proof), MPa | 600 to 910 | |
| 380 to 1000 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 440 | |
| 310 |
| Melting Completion (Liquidus), °C | 1460 | |
| 930 |
| Melting Onset (Solidus), °C | 1410 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 39 | |
| 120 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.7 | |
| 18 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 12 |
| Embodied Energy, MJ/kg | 22 | |
| 190 |
| Embodied Water, L/kg | 56 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 to 120 | |
| 11 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 950 to 2210 | |
| 590 to 4080 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 30 to 35 | |
| 21 to 36 |
| Strength to Weight: Bending, points | 25 to 28 | |
| 20 to 28 |
| Thermal Diffusivity, mm2/s | 11 | |
| 36 |
| Thermal Shock Resistance, points | 25 to 29 | |
| 23 to 39 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.15 |
| Beryllium (Be), % | 0 | |
| 2.5 to 2.9 |
| Carbon (C), % | 0.32 to 0.38 | |
| 0 |
| Chromium (Cr), % | 1.4 to 1.7 | |
| 0 to 0.1 |
| Cobalt (Co), % | 0 | |
| 0.15 to 0.7 |
| Copper (Cu), % | 0 | |
| 94.6 to 97.2 |
| Iron (Fe), % | 94.2 to 96.1 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0.6 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 0.15 to 0.35 | |
| 0 |
| Nickel (Ni), % | 1.4 to 1.7 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.6 | |
| 0.2 to 0.35 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0 | |
| 0 to 0.12 |
| Zinc (Zn), % | 0 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.5 |