EN 1.6587 Steel vs. C95410 Bronze
EN 1.6587 steel belongs to the iron alloys classification, while C95410 bronze belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.6587 steel and the bottom bar is C95410 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 220 | |
| 160 to 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 1420 | |
| 620 to 740 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 440 | |
| 230 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1040 |
| Melting Onset (Solidus), °C | 1420 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 440 |
| Thermal Conductivity, W/m-K | 41 | |
| 59 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.6 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.8 | |
| 28 |
| Density, g/cm3 | 7.9 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 3.3 |
| Embodied Energy, MJ/kg | 22 | |
| 54 |
| Embodied Water, L/kg | 58 | |
| 390 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 24 | |
| 20 |
| Strength to Weight: Axial, points | 18 to 50 | |
| 21 to 25 |
| Strength to Weight: Bending, points | 18 to 36 | |
| 20 to 22 |
| Thermal Diffusivity, mm2/s | 11 | |
| 16 |
| Thermal Shock Resistance, points | 15 to 42 | |
| 22 to 26 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 10 to 11.5 |
| Carbon (C), % | 0.15 to 0.21 | |
| 0 |
| Chromium (Cr), % | 1.5 to 1.8 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 83 to 85.5 |
| Iron (Fe), % | 94.4 to 96.4 | |
| 3.0 to 5.0 |
| Manganese (Mn), % | 0.5 to 0.9 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0.25 to 0.35 | |
| 0 |
| Nickel (Ni), % | 1.4 to 1.7 | |
| 1.5 to 2.5 |
| Oxygen (O), % | 0 to 0.0020 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |