EN 1.6750 Steel vs. EN 1.8509 Steel

Both EN 1.6750 steel and EN 1.8509 steel are iron alloys. Both are furnished in the quenched and tempered condition. They have a very high 98% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.6750 steel and the bottom bar is EN 1.8509 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
340
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 18
11
Fatigue Strength, MPa 310
580
Impact Strength: V-Notched Charpy, J 46
29
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 650
1130
Tensile Strength: Yield (Proof), MPa 460
940

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
440
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
39
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 3.3
2.8
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.7
1.6
Embodied Energy, MJ/kg 22
22
Embodied Water, L/kg 52
65

Common Calculations

PREN (Pitting Resistance) 2.4
2.6
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
120
Resilience: Unit (Modulus of Resilience), kJ/m3 570
2340
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23
40
Strength to Weight: Bending, points 21
31
Thermal Diffusivity, mm2/s 10
10
Thermal Shock Resistance, points 19
33

Alloy Composition

Aluminum (Al), % 0
0.8 to 1.2
Carbon (C), % 0.17 to 0.23
0.38 to 0.45
Chromium (Cr), % 0.3 to 0.5
1.5 to 1.8
Iron (Fe), % 95.3 to 97.5
95.5 to 97.1
Manganese (Mn), % 0.8 to 1.2
0.4 to 0.7
Molybdenum (Mo), % 0.4 to 0.8
0.2 to 0.35
Nickel (Ni), % 0.8 to 1.2
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.6
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.035