EN 1.6750 Steel vs. C17300 Copper

EN 1.6750 steel belongs to the iron alloys classification, while C17300 copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.6750 steel and the bottom bar is C17300 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 18
3.0 to 23
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
45
Tensile Strength: Ultimate (UTS), MPa 650
500 to 1380
Tensile Strength: Yield (Proof), MPa 460
160 to 1200

Thermal Properties

Latent Heat of Fusion, J/g 250
230
Maximum Temperature: Mechanical, °C 420
270
Melting Completion (Liquidus), °C 1460
980
Melting Onset (Solidus), °C 1420
870
Specific Heat Capacity, J/kg-K 470
380
Thermal Conductivity, W/m-K 39
110
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
22
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
23

Otherwise Unclassified Properties

Density, g/cm3 7.9
8.8
Embodied Carbon, kg CO2/kg material 1.7
9.4
Embodied Energy, MJ/kg 22
150
Embodied Water, L/kg 52
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
40 to 88
Resilience: Unit (Modulus of Resilience), kJ/m3 570
110 to 5410
Stiffness to Weight: Axial, points 13
7.6
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 23
16 to 44
Strength to Weight: Bending, points 21
16 to 31
Thermal Diffusivity, mm2/s 10
32
Thermal Shock Resistance, points 19
17 to 48

Alloy Composition

Aluminum (Al), % 0
0 to 0.2
Beryllium (Be), % 0
1.8 to 2.0
Carbon (C), % 0.17 to 0.23
0
Chromium (Cr), % 0.3 to 0.5
0
Copper (Cu), % 0
95.5 to 97.8
Iron (Fe), % 95.3 to 97.5
0 to 0.4
Lead (Pb), % 0
0.2 to 0.6
Manganese (Mn), % 0.8 to 1.2
0
Molybdenum (Mo), % 0.4 to 0.8
0
Nickel (Ni), % 0.8 to 1.2
0.2 to 0.6
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.6
0 to 0.2
Sulfur (S), % 0 to 0.030
0
Residuals, % 0
0 to 0.5