EN 1.6958 Steel vs. EN 1.3532 Steel
Both EN 1.6958 steel and EN 1.3532 steel are iron alloys. Their average alloy composition is basically identical. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.6958 steel and the bottom bar is EN 1.3532 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 340 | |
| 210 to 220 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 1140 | |
| 700 to 1420 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 450 | |
| 440 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 47 | |
| 46 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.9 | |
| 7.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.1 | |
| 9.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 5.0 | |
| 5.0 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 1.9 |
| Embodied Energy, MJ/kg | 27 | |
| 25 |
| Embodied Water, L/kg | 60 | |
| 60 |
Common Calculations
| PREN (Pitting Resistance) | 2.9 | |
| 2.0 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 40 | |
| 25 to 50 |
| Strength to Weight: Bending, points | 31 | |
| 22 to 36 |
| Thermal Diffusivity, mm2/s | 13 | |
| 13 |
| Thermal Shock Resistance, points | 39 | |
| 21 to 42 |
Alloy Composition
| Aluminum (Al), % | 0.0050 to 0.050 | |
| 0 to 0.050 |
| Carbon (C), % | 0.25 to 0.3 | |
| 0.14 to 0.18 |
| Chromium (Cr), % | 1.2 to 1.7 | |
| 1.0 to 1.4 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 92.6 to 94.5 | |
| 92.6 to 94.8 |
| Manganese (Mn), % | 0.2 to 0.5 | |
| 0.25 to 0.55 |
| Molybdenum (Mo), % | 0.35 to 0.55 | |
| 0.2 to 0.3 |
| Nickel (Ni), % | 3.3 to 3.8 | |
| 3.8 to 4.3 |
| Oxygen (O), % | 0 | |
| 0 to 0.0020 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.15 to 0.3 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 to 0.12 | |
| 0 |