EN 1.6982 Stainless Steel vs. AWS E430Nb

Both EN 1.6982 stainless steel and AWS E430Nb are iron alloys. They have a moderately high 95% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.6982 stainless steel and the bottom bar is AWS E430Nb.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 17
23
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 800
500

Thermal Properties

Latent Heat of Fusion, J/g 280
280
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 25
24
Thermal Expansion, µm/m-K 10
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.7
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 3.2
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 10
15
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.4
3.1
Embodied Energy, MJ/kg 33
45
Embodied Water, L/kg 110
120

Common Calculations

PREN (Pitting Resistance) 14
18
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 28
18
Strength to Weight: Bending, points 25
18
Thermal Diffusivity, mm2/s 6.6
6.6
Thermal Shock Resistance, points 29
13

Alloy Composition

Carbon (C), % 0 to 0.050
0 to 0.1
Chromium (Cr), % 12 to 13.5
15 to 18
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 78.7 to 84.5
76.2 to 84.5
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.7
0 to 0.75
Nickel (Ni), % 3.5 to 5.0
0 to 0.6
Niobium (Nb), % 0
0.5 to 1.5
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030