EN 1.7016 Steel vs. Grade Ti-Pd7B Titanium
EN 1.7016 steel belongs to the iron alloys classification, while grade Ti-Pd7B titanium belongs to the titanium alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.7016 steel and the bottom bar is grade Ti-Pd7B titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 130 to 170 | |
| 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 73 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 450 to 1390 | |
| 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 320 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1660 |
| Melting Onset (Solidus), °C | 1420 | |
| 1610 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 540 |
| Thermal Conductivity, W/m-K | 45 | |
| 22 |
| Thermal Expansion, µm/m-K | 13 | |
| 8.7 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 3.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 7.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 49 |
| Embodied Energy, MJ/kg | 19 | |
| 840 |
| Embodied Water, L/kg | 50 | |
| 520 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 35 |
| Strength to Weight: Axial, points | 16 to 49 | |
| 24 |
| Strength to Weight: Bending, points | 17 to 35 | |
| 26 |
| Thermal Diffusivity, mm2/s | 12 | |
| 8.9 |
| Thermal Shock Resistance, points | 13 to 41 | |
| 30 |
Alloy Composition
| Carbon (C), % | 0.14 to 0.2 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0.7 to 1.0 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 97.3 to 98.6 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.4 |
| Palladium (Pd), % | 0 | |
| 0.12 to 0.3 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 98.8 to 99.9 |
| Residuals, % | 0 | |
| 0 to 0.4 |