EN 1.7016 Steel vs. SAE-AISI 1137 Steel
Both EN 1.7016 steel and SAE-AISI 1137 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.7016 steel and the bottom bar is SAE-AISI 1137 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 130 to 170 | |
| 200 to 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 450 to 1390 | |
| 700 to 760 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 45 | |
| 51 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 10 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.2 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 19 | |
| 19 |
| Embodied Water, L/kg | 50 | |
| 48 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 16 to 49 | |
| 25 to 27 |
| Strength to Weight: Bending, points | 17 to 35 | |
| 22 to 24 |
| Thermal Diffusivity, mm2/s | 12 | |
| 14 |
| Thermal Shock Resistance, points | 13 to 41 | |
| 21 to 23 |
Alloy Composition
| Carbon (C), % | 0.14 to 0.2 | |
| 0.32 to 0.39 |
| Chromium (Cr), % | 0.7 to 1.0 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 97.3 to 98.6 | |
| 97.8 to 98.3 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 1.4 to 1.7 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0.080 to 0.13 |