EN 1.7016 Steel vs. N10001 Nickel

EN 1.7016 steel belongs to the iron alloys classification, while N10001 nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.7016 steel and the bottom bar is N10001 nickel.

EN 1.7016 (17Cr3) Chromium Steel UNS N10001 (2.4810) Nickel-Molybdenum Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		220

Poisson's Ratio		0.29
Poisson's Ratio		0.31

Shear Modulus, GPa		73
Shear Modulus, GPa		84

Tensile Strength: Ultimate (UTS), MPa		450 to 1390
Tensile Strength: Ultimate (UTS), MPa		780

Thermal Properties

Latent Heat of Fusion, J/g		250
Latent Heat of Fusion, J/g		320

Maximum Temperature: Mechanical, °C		420
Maximum Temperature: Mechanical, °C		900

Melting Completion (Liquidus), °C		1460
Melting Completion (Liquidus), °C		1620

Melting Onset (Solidus), °C		1420
Melting Onset (Solidus), °C		1570

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		390

Thermal Expansion, µm/m-K		13
Thermal Expansion, µm/m-K		10

Otherwise Unclassified Properties

Base Metal Price, % relative		2.2
Base Metal Price, % relative		75

Density, g/cm³		7.8
Density, g/cm³		9.2

Embodied Carbon, kg CO₂/kg material		1.4
Embodied Carbon, kg CO₂/kg material		15

Embodied Energy, MJ/kg		19
Embodied Energy, MJ/kg		200

Embodied Water, L/kg		50
Embodied Water, L/kg		260

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		22

Strength to Weight: Axial, points		16 to 49
Strength to Weight: Axial, points		24

Strength to Weight: Bending, points		17 to 35
Strength to Weight: Bending, points		21

Thermal Shock Resistance, points		13 to 41
Thermal Shock Resistance, points		25

Alloy Composition

Carbon (C), %		0.14 to 0.2
Carbon (C), %		0 to 0.050

Chromium (Cr), %		0.7 to 1.0
Chromium (Cr), %		0 to 1.0

Cobalt (Co), %		0
Cobalt (Co), %		0 to 2.5

Copper (Cu), %		0 to 0.25
Copper (Cu), %		0

Iron (Fe), %		97.3 to 98.6
Iron (Fe), %		4.0 to 6.0

Manganese (Mn), %		0.6 to 0.9
Manganese (Mn), %		0 to 1.0

Molybdenum (Mo), %		0
Molybdenum (Mo), %		26 to 30

Nickel (Ni), %		0
Nickel (Ni), %		58 to 69.8

Phosphorus (P), %		0 to 0.025
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0 to 0.3
Silicon (Si), %		0 to 1.0

Sulfur (S), %		0 to 0.025
Sulfur (S), %		0 to 0.030

Vanadium (V), %		0
Vanadium (V), %		0.2 to 0.4