EN 1.7034 Steel vs. EN 1.4901 Stainless Steel
Both EN 1.7034 steel and EN 1.4901 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is EN 1.7034 steel and the bottom bar is EN 1.4901 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 510 to 1780 | |
| 740 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 650 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1490 |
| Melting Onset (Solidus), °C | 1420 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 45 | |
| 26 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 8.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 9.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.2 | |
| 11 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.8 |
| Embodied Energy, MJ/kg | 19 | |
| 40 |
| Embodied Water, L/kg | 50 | |
| 89 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 18 to 63 | |
| 26 |
| Strength to Weight: Bending, points | 18 to 42 | |
| 23 |
| Thermal Diffusivity, mm2/s | 12 | |
| 6.9 |
| Thermal Shock Resistance, points | 15 to 52 | |
| 23 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.020 |
| Boron (B), % | 0 | |
| 0.0010 to 0.0060 |
| Carbon (C), % | 0.34 to 0.41 | |
| 0.070 to 0.13 |
| Chromium (Cr), % | 0.9 to 1.2 | |
| 8.5 to 9.5 |
| Iron (Fe), % | 97 to 98.2 | |
| 85.8 to 89.1 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 0 | |
| 0.3 to 0.6 |
| Nickel (Ni), % | 0 | |
| 0 to 0.4 |
| Niobium (Nb), % | 0 | |
| 0.040 to 0.090 |
| Nitrogen (N), % | 0 | |
| 0.030 to 0.070 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.035 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 1.5 to 2.0 |
| Vanadium (V), % | 0 | |
| 0.15 to 0.25 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.010 |