EN 1.7076 Steel vs. EN 1.7039 Steel
Both EN 1.7076 steel and EN 1.7039 steel are iron alloys. Their average alloy composition is basically identical. There are 24 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 1.7076 steel and the bottom bar is EN 1.7039 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 470 to 1700 | |
| 530 to 1850 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 420 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 45 | |
| 46 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.3 | |
| 2.3 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 19 | |
| 19 |
| Embodied Water, L/kg | 51 | |
| 51 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 17 to 60 | |
| 19 to 65 |
| Strength to Weight: Bending, points | 17 to 40 | |
| 19 to 43 |
| Thermal Diffusivity, mm2/s | 12 | |
| 12 |
| Thermal Shock Resistance, points | 14 to 50 | |
| 16 to 54 |
Alloy Composition
| Boron (B), % | 0.00080 to 0.0050 | |
| 0 |
| Carbon (C), % | 0.3 to 0.34 | |
| 0.38 to 0.45 |
| Chromium (Cr), % | 0.9 to 1.2 | |
| 0.9 to 1.2 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.25 |
| Iron (Fe), % | 97 to 98.2 | |
| 96.8 to 98.1 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0.6 to 0.9 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.025 | |
| 0.020 to 0.040 |