EN 1.7102 Steel vs. Grade CX2M Nickel

EN 1.7102 steel belongs to the iron alloys classification, while grade CX2M nickel belongs to the nickel alloys. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.7102 steel and the bottom bar is grade CX2M nickel.

EN 1.7102 (54SiCr6) Silicon-Chromium Steel Grade CX2M (N26059) Cast Nickel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		220

Poisson's Ratio		0.29
Poisson's Ratio		0.29

Shear Modulus, GPa		72
Shear Modulus, GPa		84

Tensile Strength: Ultimate (UTS), MPa		670 to 2010
Tensile Strength: Ultimate (UTS), MPa		550

Thermal Properties

Latent Heat of Fusion, J/g		270
Latent Heat of Fusion, J/g		330

Maximum Temperature: Mechanical, °C		410
Maximum Temperature: Mechanical, °C		990

Melting Completion (Liquidus), °C		1440
Melting Completion (Liquidus), °C		1500

Melting Onset (Solidus), °C		1400
Melting Onset (Solidus), °C		1450

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		430

Thermal Conductivity, W/m-K		47
Thermal Conductivity, W/m-K		10

Thermal Expansion, µm/m-K		13
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		2.2
Base Metal Price, % relative		65

Density, g/cm³		7.7
Density, g/cm³		8.7

Embodied Carbon, kg CO₂/kg material		1.5
Embodied Carbon, kg CO₂/kg material		12

Embodied Energy, MJ/kg		20
Embodied Energy, MJ/kg		160

Embodied Water, L/kg		48
Embodied Water, L/kg		310

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		24 to 72
Strength to Weight: Axial, points		18

Strength to Weight: Bending, points		22 to 46
Strength to Weight: Bending, points		17

Thermal Diffusivity, mm²/s		13
Thermal Diffusivity, mm²/s		2.7

Thermal Shock Resistance, points		20 to 60
Thermal Shock Resistance, points		15

Alloy Composition

Carbon (C), %		0.51 to 0.59
Carbon (C), %		0 to 0.020

Chromium (Cr), %		0.5 to 0.8
Chromium (Cr), %		22 to 24

Iron (Fe), %		96.2 to 97.3
Iron (Fe), %		0 to 1.5

Manganese (Mn), %		0.5 to 0.8
Manganese (Mn), %		0 to 1.0

Molybdenum (Mo), %		0
Molybdenum (Mo), %		15 to 16.5

Nickel (Ni), %		0
Nickel (Ni), %		56.4 to 63

Phosphorus (P), %		0 to 0.025
Phosphorus (P), %		0 to 0.020

Silicon (Si), %		1.2 to 1.6
Silicon (Si), %		0 to 0.5

Sulfur (S), %		0 to 0.025
Sulfur (S), %		0 to 0.020