EN 1.7106 Steel vs. C10400 Copper
EN 1.7106 steel belongs to the iron alloys classification, while C10400 copper belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.7106 steel and the bottom bar is C10400 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 72 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 2020 | |
| 230 to 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 200 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1080 |
| Melting Onset (Solidus), °C | 1390 | |
| 1080 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Conductivity, W/m-K | 46 | |
| 390 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 100 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 32 |
| Density, g/cm3 | 7.7 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 2.6 |
| Embodied Energy, MJ/kg | 20 | |
| 42 |
| Embodied Water, L/kg | 47 | |
| 340 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 24 to 73 | |
| 7.2 to 13 |
| Strength to Weight: Bending, points | 22 to 46 | |
| 9.4 to 14 |
| Thermal Diffusivity, mm2/s | 13 | |
| 110 |
| Thermal Shock Resistance, points | 20 to 61 | |
| 8.2 to 15 |
Alloy Composition
| Carbon (C), % | 0.52 to 0.6 | |
| 0 |
| Chromium (Cr), % | 0.2 to 0.45 | |
| 0 |
| Copper (Cu), % | 0 | |
| 99.9 to 99.973 |
| Iron (Fe), % | 95.9 to 97 | |
| 0 |
| Manganese (Mn), % | 0.7 to 1.0 | |
| 0 |
| Oxygen (O), % | 0 | |
| 0 to 0.0010 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 1.6 to 2.0 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0.027 to 0.050 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.050 |