EN 1.7131 Steel vs. N12160 Nickel
EN 1.7131 steel belongs to the iron alloys classification, while N12160 nickel belongs to the nickel alloys. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is EN 1.7131 steel and the bottom bar is N12160 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 470 to 1390 | |
| 710 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 360 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 1060 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1330 |
| Melting Onset (Solidus), °C | 1420 | |
| 1280 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 45 | |
| 11 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.2 | |
| 90 |
| Density, g/cm3 | 7.8 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 8.5 |
| Embodied Energy, MJ/kg | 19 | |
| 120 |
| Embodied Water, L/kg | 51 | |
| 400 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 17 to 49 | |
| 24 |
| Strength to Weight: Bending, points | 17 to 35 | |
| 22 |
| Thermal Diffusivity, mm2/s | 12 | |
| 2.8 |
| Thermal Shock Resistance, points | 14 to 41 | |
| 19 |
Alloy Composition
| Carbon (C), % | 0.14 to 0.19 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0.8 to 1.1 | |
| 26 to 30 |
| Cobalt (Co), % | 0 | |
| 27 to 33 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 96.8 to 98.1 | |
| 0 to 3.5 |
| Manganese (Mn), % | 1.0 to 1.3 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 25 to 44.4 |
| Niobium (Nb), % | 0 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.3 | |
| 2.4 to 3.0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0.2 to 0.8 |
| Tungsten (W), % | 0 | |
| 0 to 1.0 |