EN 1.7149 Steel vs. EN 1.4423 Stainless Steel

Both EN 1.7149 steel and EN 1.4423 stainless steel are iron alloys. They have 80% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.7149 steel and the bottom bar is EN 1.4423 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 500 to 1460
850

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 420
780
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 46
16
Thermal Expansion, µm/m-K 13
9.9

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
14
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
3.2
Embodied Energy, MJ/kg 19
43
Embodied Water, L/kg 52
120

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18 to 52
30
Strength to Weight: Bending, points 18 to 36
25
Thermal Diffusivity, mm2/s 12
4.3
Thermal Shock Resistance, points 15 to 42
31

Alloy Composition

Carbon (C), % 0.17 to 0.22
0 to 0.020
Chromium (Cr), % 1.0 to 1.3
11 to 13
Copper (Cu), % 0 to 0.25
0.2 to 0.8
Iron (Fe), % 96.5 to 97.7
73.8 to 80.5
Manganese (Mn), % 1.1 to 1.4
0 to 2.0
Molybdenum (Mo), % 0
2.3 to 2.8
Nickel (Ni), % 0
6.0 to 7.0
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.3
0 to 0.5
Sulfur (S), % 0.020 to 0.040
0 to 0.0030