EN 1.7176 Steel vs. AWS E209
Both EN 1.7176 steel and AWS E209 are iron alloys. They have 60% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.7176 steel and the bottom bar is AWS E209.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
200 |
Poisson's Ratio | 0.29 | |
0.28 |
Shear Modulus, GPa | 73 | |
79 |
Tensile Strength: Ultimate (UTS), MPa | 670 to 2010 | |
770 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
300 |
Melting Completion (Liquidus), °C | 1450 | |
1420 |
Melting Onset (Solidus), °C | 1410 | |
1370 |
Specific Heat Capacity, J/kg-K | 470 | |
480 |
Thermal Expansion, µm/m-K | 13 | |
14 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 2.1 | |
21 |
Density, g/cm3 | 7.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
4.4 |
Embodied Energy, MJ/kg | 19 | |
63 |
Embodied Water, L/kg | 50 | |
180 |
Common Calculations
Stiffness to Weight: Axial, points | 13 | |
14 |
Stiffness to Weight: Bending, points | 24 | |
25 |
Strength to Weight: Axial, points | 24 to 71 | |
28 |
Strength to Weight: Bending, points | 22 to 45 | |
24 |
Thermal Shock Resistance, points | 20 to 59 | |
19 |
Alloy Composition
Carbon (C), % | 0.52 to 0.59 | |
0 to 0.060 |
Chromium (Cr), % | 0.7 to 1.0 | |
20.5 to 24 |
Copper (Cu), % | 0 | |
0 to 0.75 |
Iron (Fe), % | 97 to 98.1 | |
51.5 to 64.3 |
Manganese (Mn), % | 0.7 to 1.0 | |
4.0 to 7.0 |
Molybdenum (Mo), % | 0 | |
1.5 to 3.0 |
Nickel (Ni), % | 0 | |
9.5 to 12 |
Nitrogen (N), % | 0 | |
0.1 to 0.3 |
Phosphorus (P), % | 0 to 0.025 | |
0 to 0.040 |
Silicon (Si), % | 0 to 0.4 | |
0 to 1.0 |
Sulfur (S), % | 0 to 0.025 | |
0 to 0.030 |
Vanadium (V), % | 0 | |
0.1 to 0.3 |