EN 1.7202 Steel vs. EN 1.8912 Steel

Both EN 1.7202 steel and EN 1.8912 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.7202 steel and the bottom bar is EN 1.8912 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 530 to 1810
600

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
410
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 46
46
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
2.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.8
Embodied Energy, MJ/kg 20
24
Embodied Water, L/kg 51
51

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19 to 64
21
Strength to Weight: Bending, points 19 to 42
20
Thermal Diffusivity, mm2/s 12
12
Thermal Shock Resistance, points 16 to 53
18

Alloy Composition

Aluminum (Al), % 0
0 to 0.015
Carbon (C), % 0.35 to 0.4
0 to 0.22
Chromium (Cr), % 0.9 to 1.2
0 to 0.35
Copper (Cu), % 0 to 0.25
0 to 0.6
Iron (Fe), % 96.6 to 98
95 to 99.05
Manganese (Mn), % 0.6 to 0.9
1.0 to 1.8
Molybdenum (Mo), % 0.15 to 0.3
0 to 0.13
Nickel (Ni), % 0
0 to 0.85
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0
0 to 0.027
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.3
0 to 0.65
Sulfur (S), % 0 to 0.025
0 to 0.025
Titanium (Ti), % 0
0 to 0.060
Vanadium (V), % 0
0 to 0.22