EN 1.7216 Steel vs. S35000 Stainless Steel
Both EN 1.7216 steel and S35000 stainless steel are iron alloys. They have 77% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.7216 steel and the bottom bar is S35000 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 12 to 23 | |
| 2.3 to 14 |
| Fatigue Strength, MPa | 290 to 440 | |
| 380 to 520 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 78 |
| Shear Strength, MPa | 410 to 560 | |
| 740 to 950 |
| Tensile Strength: Ultimate (UTS), MPa | 650 to 930 | |
| 1300 to 1570 |
| Tensile Strength: Yield (Proof), MPa | 400 to 690 | |
| 660 to 1160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 900 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 46 | |
| 16 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 2.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 14 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 3.2 |
| Embodied Energy, MJ/kg | 20 | |
| 44 |
| Embodied Water, L/kg | 50 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 130 | |
| 28 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 430 to 1280 | |
| 1070 to 3360 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 23 to 33 | |
| 46 to 56 |
| Strength to Weight: Bending, points | 21 to 27 | |
| 34 to 38 |
| Thermal Diffusivity, mm2/s | 12 | |
| 4.4 |
| Thermal Shock Resistance, points | 19 to 27 | |
| 42 to 51 |
Alloy Composition
| Carbon (C), % | 0.27 to 0.34 | |
| 0.070 to 0.11 |
| Chromium (Cr), % | 0.8 to 1.2 | |
| 16 to 17 |
| Iron (Fe), % | 97.2 to 98.4 | |
| 72.7 to 76.9 |
| Manganese (Mn), % | 0.35 to 0.6 | |
| 0.5 to 1.3 |
| Molybdenum (Mo), % | 0.15 to 0.3 | |
| 2.5 to 3.2 |
| Nickel (Ni), % | 0 | |
| 4.0 to 5.0 |
| Nitrogen (N), % | 0 | |
| 0.070 to 0.13 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.035 | |
| 0 to 0.030 |