EN 1.7219 Steel vs. CC493K Bronze

EN 1.7219 steel belongs to the iron alloys classification, while CC493K bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.7219 steel and the bottom bar is CC493K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
74
Elastic (Young's, Tensile) Modulus, GPa 190
100
Elongation at Break, % 19
14
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
39
Tensile Strength: Ultimate (UTS), MPa 650
270
Tensile Strength: Yield (Proof), MPa 490
140

Thermal Properties

Latent Heat of Fusion, J/g 250
180
Maximum Temperature: Mechanical, °C 420
160
Melting Completion (Liquidus), °C 1460
960
Melting Onset (Solidus), °C 1420
880
Specific Heat Capacity, J/kg-K 470
360
Thermal Conductivity, W/m-K 44
61
Thermal Expansion, µm/m-K 13
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
12
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
12

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
32
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 1.5
3.3
Embodied Energy, MJ/kg 20
53
Embodied Water, L/kg 51
370

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
33
Resilience: Unit (Modulus of Resilience), kJ/m3 650
89
Stiffness to Weight: Axial, points 13
6.5
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 23
8.6
Strength to Weight: Bending, points 21
11
Thermal Diffusivity, mm2/s 12
19
Thermal Shock Resistance, points 19
10

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Antimony (Sb), % 0
0 to 0.3
Carbon (C), % 0.22 to 0.29
0
Chromium (Cr), % 0.9 to 1.2
0
Copper (Cu), % 0 to 0.3
79 to 86
Iron (Fe), % 96.7 to 98.2
0 to 0.2
Lead (Pb), % 0
5.0 to 8.0
Manganese (Mn), % 0.5 to 0.8
0
Molybdenum (Mo), % 0.15 to 0.3
0
Nickel (Ni), % 0
0 to 2.0
Phosphorus (P), % 0 to 0.025
0 to 0.1
Silicon (Si), % 0 to 0.35
0 to 0.010
Sulfur (S), % 0 to 0.010
0 to 0.1
Tin (Sn), % 0
5.2 to 8.0
Zinc (Zn), % 0
2.0 to 5.0