EN 1.7220 Steel vs. EN 2.4642 Nickel
EN 1.7220 steel belongs to the iron alloys classification, while EN 2.4642 nickel belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.7220 steel and the bottom bar is EN 2.4642 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 1720 | |
| 670 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 1010 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1360 |
| Melting Onset (Solidus), °C | 1420 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 44 | |
| 12 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.5 | |
| 50 |
| Density, g/cm3 | 7.8 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 8.2 |
| Embodied Energy, MJ/kg | 20 | |
| 120 |
| Embodied Water, L/kg | 51 | |
| 290 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 18 to 61 | |
| 23 |
| Strength to Weight: Bending, points | 18 to 41 | |
| 21 |
| Thermal Diffusivity, mm2/s | 12 | |
| 3.1 |
| Thermal Shock Resistance, points | 15 to 50 | |
| 18 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.5 |
| Carbon (C), % | 0.3 to 0.37 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0.9 to 1.2 | |
| 27 to 31 |
| Copper (Cu), % | 0 | |
| 0 to 0.5 |
| Iron (Fe), % | 96.8 to 98.1 | |
| 7.0 to 11 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0.15 to 0.3 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 55.9 to 66 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.035 | |
| 0 to 0.015 |