EN 1.7221 Steel vs. EN 1.7362 Steel
Both EN 1.7221 steel and EN 1.7362 steel are iron alloys. They have a very high 95% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 1.7221 steel and the bottom bar is EN 1.7362 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 230 | |
| 150 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 11 to 17 | |
| 21 to 22 |
| Fatigue Strength, MPa | 290 to 390 | |
| 140 to 250 |
| Impact Strength: V-Notched Charpy, J | 20 to 38 | |
| 38 to 46 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 650 to 780 | |
| 510 to 600 |
| Tensile Strength: Yield (Proof), MPa | 430 to 630 | |
| 200 to 360 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 510 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 44 | |
| 40 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 8.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 9.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 4.5 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.8 |
| Embodied Energy, MJ/kg | 20 | |
| 23 |
| Embodied Water, L/kg | 51 | |
| 69 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 83 to 98 | |
| 90 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 490 to 1050 | |
| 100 to 340 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 23 to 27 | |
| 18 to 21 |
| Strength to Weight: Bending, points | 21 to 24 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 12 | |
| 11 |
| Thermal Shock Resistance, points | 19 to 23 | |
| 14 to 17 |
Alloy Composition
| Carbon (C), % | 0.22 to 0.29 | |
| 0.1 to 0.15 |
| Chromium (Cr), % | 0.8 to 1.2 | |
| 4.0 to 6.0 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 96.8 to 98.3 | |
| 91.5 to 95.2 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 0.15 to 0.3 | |
| 0.45 to 0.65 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Nitrogen (N), % | 0 | |
| 0 to 0.012 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.0050 |