EN 1.7221 Steel vs. Grade 20 Titanium
EN 1.7221 steel belongs to the iron alloys classification, while grade 20 titanium belongs to the titanium alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is EN 1.7221 steel and the bottom bar is grade 20 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
120 |
Elongation at Break, % | 11 to 17 | |
5.7 to 17 |
Fatigue Strength, MPa | 290 to 390 | |
550 to 630 |
Poisson's Ratio | 0.29 | |
0.32 |
Shear Modulus, GPa | 73 | |
47 |
Tensile Strength: Ultimate (UTS), MPa | 650 to 780 | |
900 to 1270 |
Tensile Strength: Yield (Proof), MPa | 430 to 630 | |
850 to 1190 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
400 |
Maximum Temperature: Mechanical, °C | 420 | |
370 |
Melting Completion (Liquidus), °C | 1460 | |
1660 |
Melting Onset (Solidus), °C | 1420 | |
1600 |
Specific Heat Capacity, J/kg-K | 470 | |
520 |
Thermal Expansion, µm/m-K | 13 | |
9.6 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.8 | |
5.0 |
Embodied Carbon, kg CO2/kg material | 1.5 | |
52 |
Embodied Energy, MJ/kg | 20 | |
860 |
Embodied Water, L/kg | 51 | |
350 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 83 to 98 | |
71 to 150 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 490 to 1050 | |
2940 to 5760 |
Stiffness to Weight: Axial, points | 13 | |
14 |
Stiffness to Weight: Bending, points | 24 | |
33 |
Strength to Weight: Axial, points | 23 to 27 | |
50 to 70 |
Strength to Weight: Bending, points | 21 to 24 | |
41 to 52 |
Thermal Shock Resistance, points | 19 to 23 | |
55 to 77 |
Alloy Composition
Aluminum (Al), % | 0 | |
3.0 to 4.0 |
Carbon (C), % | 0.22 to 0.29 | |
0 to 0.050 |
Chromium (Cr), % | 0.8 to 1.2 | |
5.5 to 6.5 |
Hydrogen (H), % | 0 | |
0 to 0.020 |
Iron (Fe), % | 96.8 to 98.3 | |
0 to 0.3 |
Manganese (Mn), % | 0.5 to 0.8 | |
0 |
Molybdenum (Mo), % | 0.15 to 0.3 | |
3.5 to 4.5 |
Nitrogen (N), % | 0 | |
0 to 0.030 |
Oxygen (O), % | 0 | |
0 to 0.12 |
Palladium (Pd), % | 0 | |
0.040 to 0.080 |
Phosphorus (P), % | 0 to 0.025 | |
0 |
Silicon (Si), % | 0 to 0.6 | |
0 |
Sulfur (S), % | 0 to 0.030 | |
0 |
Titanium (Ti), % | 0 | |
71 to 77 |
Vanadium (V), % | 0 | |
7.5 to 8.5 |
Zirconium (Zr), % | 0 | |
3.5 to 4.5 |
Residuals, % | 0 | |
0 to 0.4 |