EN 1.7221 Steel vs. N06650 Nickel
EN 1.7221 steel belongs to the iron alloys classification, while N06650 nickel belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.7221 steel and the bottom bar is N06650 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 11 to 17 | |
| 50 |
| Fatigue Strength, MPa | 290 to 390 | |
| 420 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 82 |
| Tensile Strength: Ultimate (UTS), MPa | 650 to 780 | |
| 900 |
| Tensile Strength: Yield (Proof), MPa | 430 to 630 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 980 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1500 |
| Melting Onset (Solidus), °C | 1420 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 440 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 60 |
| Density, g/cm3 | 7.8 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 10 |
| Embodied Energy, MJ/kg | 20 | |
| 140 |
| Embodied Water, L/kg | 51 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 83 to 98 | |
| 380 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 490 to 1050 | |
| 490 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 23 to 27 | |
| 29 |
| Strength to Weight: Bending, points | 21 to 24 | |
| 24 |
| Thermal Shock Resistance, points | 19 to 23 | |
| 24 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.050 to 0.5 |
| Carbon (C), % | 0.22 to 0.29 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0.8 to 1.2 | |
| 19 to 21 |
| Cobalt (Co), % | 0 | |
| 0 to 1.0 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 96.8 to 98.3 | |
| 12 to 16 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0.15 to 0.3 | |
| 9.5 to 12.5 |
| Nickel (Ni), % | 0 | |
| 44.4 to 58.9 |
| Niobium (Nb), % | 0 | |
| 0.050 to 0.5 |
| Nitrogen (N), % | 0 | |
| 0.050 to 0.2 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 0.5 to 2.5 |