EN 1.7228 Steel vs. AWS E320

Both EN 1.7228 steel and AWS E320 are iron alloys. They have a modest 40% of their average alloy composition in common, which, by itself, doesn't mean much. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is EN 1.7228 steel and the bottom bar is AWS E320.

EN 1.7228 (50CrMo4) Chromium-Molybdenum Steel AWS E320 (W88021) Weld Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		200

Elongation at Break, %		12
Elongation at Break, %		34

Poisson's Ratio		0.29
Poisson's Ratio		0.28

Shear Modulus, GPa		73
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		900
Tensile Strength: Ultimate (UTS), MPa		620

Thermal Properties

Latent Heat of Fusion, J/g		250
Latent Heat of Fusion, J/g		300

Melting Completion (Liquidus), °C		1460
Melting Completion (Liquidus), °C		1410

Melting Onset (Solidus), °C		1420
Melting Onset (Solidus), °C		1360

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		460

Thermal Expansion, µm/m-K		13
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Base Metal Price, % relative		2.5
Base Metal Price, % relative		38

Density, g/cm³		7.8
Density, g/cm³		8.2

Embodied Carbon, kg CO₂/kg material		1.5
Embodied Carbon, kg CO₂/kg material		6.5

Embodied Energy, MJ/kg		20
Embodied Energy, MJ/kg		91

Embodied Water, L/kg		51
Embodied Water, L/kg		220

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		32
Strength to Weight: Axial, points		21

Strength to Weight: Bending, points		26
Strength to Weight: Bending, points		20

Thermal Shock Resistance, points		26
Thermal Shock Resistance, points		16

Alloy Composition

Carbon (C), %		0.46 to 0.54
Carbon (C), %		0 to 0.070

Chromium (Cr), %		0.9 to 1.2
Chromium (Cr), %		19 to 21

Copper (Cu), %		0
Copper (Cu), %		3.0 to 4.0

Iron (Fe), %		96.7 to 98
Iron (Fe), %		31.8 to 43.5

Manganese (Mn), %		0.5 to 0.8
Manganese (Mn), %		0.5 to 2.5

Molybdenum (Mo), %		0.15 to 0.3
Molybdenum (Mo), %		2.0 to 3.0

Nickel (Ni), %		0
Nickel (Ni), %		32 to 36

Niobium (Nb), %		0
Niobium (Nb), %		0 to 1.0

Phosphorus (P), %		0 to 0.035
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0 to 0.4
Silicon (Si), %		0 to 0.6

Sulfur (S), %		0 to 0.035
Sulfur (S), %		0 to 0.030