EN 1.7230 Steel vs. EN 1.7767 Steel
Both EN 1.7230 steel and EN 1.7767 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 1.7230 steel and the bottom bar is EN 1.7767 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 220 to 270 | |
| 200 to 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 11 to 12 | |
| 20 |
| Fatigue Strength, MPa | 320 to 460 | |
| 320 to 340 |
| Impact Strength: V-Notched Charpy, J | 29 to 30 | |
| 46 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 720 to 910 | |
| 670 to 690 |
| Tensile Strength: Yield (Proof), MPa | 510 to 740 | |
| 460 to 500 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 480 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1470 |
| Melting Onset (Solidus), °C | 1420 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 44 | |
| 40 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 7.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 8.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 4.5 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 2.4 |
| Embodied Energy, MJ/kg | 20 | |
| 33 |
| Embodied Water, L/kg | 51 | |
| 64 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 79 to 97 | |
| 120 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 700 to 1460 | |
| 570 to 650 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 26 to 32 | |
| 24 |
| Strength to Weight: Bending, points | 23 to 27 | |
| 22 |
| Thermal Diffusivity, mm2/s | 12 | |
| 11 |
| Thermal Shock Resistance, points | 21 to 27 | |
| 19 to 20 |
Alloy Composition
| Carbon (C), % | 0.3 to 0.37 | |
| 0.1 to 0.15 |
| Chromium (Cr), % | 0.8 to 1.2 | |
| 2.8 to 3.3 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 96.7 to 98.3 | |
| 93.8 to 95.8 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 0.15 to 0.3 | |
| 0.9 to 1.1 |
| Nickel (Ni), % | 0 | |
| 0 to 0.25 |
| Niobium (Nb), % | 0 | |
| 0 to 0.070 |
| Nitrogen (N), % | 0 | |
| 0 to 0.012 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 to 0.15 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.0050 |
| Titanium (Ti), % | 0 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 0.2 to 0.3 |